C1000 METAL DOCTOR BLADE

Ceramic-Coated Doctor Blades
C1000 (2067 Carbon Steel)
  • C1000 (2067 Carbon Steel)
  • C1000 (2067 Carbon Steel)
  • C1000 (2067 Carbon Steel)
Request a Quote
Blade Edge Shapes
  • Lamella Blade Edge
  • Bevel Blade Edge
Specifications
Width range: 10mm-60mm
Width tolerance: ±0.1mm
Thickness range: 0.152mm-0.3mm
Thickness tolerance: ±0.005mm
Hardness: 780-810HV
Tensile strength: 1850-2100Pa
Straightness: ≤0.5mm/3000mm
Coating thickness: 6-8μm
Dimensions
  • 10mm×0.15mm×100m
  • 20mm×0.15mm×100m
  • 20mm×0.2mm×100m
  • 30mm×0.15mm×100m
  • 30mm×0.2mm×100m
  • 35mm×0.15mm×100m
  • 35mm×0.2mm×100m
  • 40mm×0.15mm×100m
  • 40mm×0.2mm×100m
  • 40mm×0.3mm×100m
  • 50mm×0.15mm×100m
  • 50mm×0.2mm×100m
  • 60mm×0.15mm×100m
  • 60mm×0.2mm×100m
The listed specifications are standard sizes. Customized dimensions can be provided upon request to meet specific printing requirements.
Applications
These metal doctor blades perform well with corrosive and solvent-based inks, maintaining stability in chemically reactive printing environments.
Their strong wear resistance makes them suitable for printing plates with high hardness, ensuring consistent performance without excessive blade wear.
In varnish and specialty ink printing, these doctor blades maintain ink stability, ensuring reliable performance in high-gloss and spot color applications.
Widely used in full coverage, spot color, and corrugated printing, supporting print jobs that require precise ink metering and extended durability.
Features
The high-hardness structure (HV800) provides strong resistance to wear and corrosion, preventing color inconsistencies and unwanted streaks caused by ink impurities.
The ceramic coating enhances durability, ensuring a smooth and stable blade edge over extended use.
Consistent ink control supports precise color transitions, reducing tonal shifts and minimizing defects such as fine lines or blade marks.

This series of doctor blades are made from 2067 carbon steel and feature a specialized ceramic coating with a thickness of 6-8μm, enhancing wear resistance and extending operational lifespan. Capable of handling press speeds of up to 400m/min, they maintain color consistency by minimizing the impact of edge wear on ink transitions over long print runs.
Find the Best Doctor Blade for Your Printing Needs. Contact Us Now!
Email: 18255555333@163.com
Mobile: +86-18255555333

The ceramic coating enhances wear resistance, extending the blade's lifespan to over 100,000 meters. With added corrosion resistance, these blades help reduce color inconsistencies, ink drag, and streaking, ensuring sharp and precise prints even in demanding applications.

These blades are commonly used in gravure and flexographic printing, excelling in spot color, full coverage, and high-gloss printing. The ceramic layer helps compensate for the wear limitations of other blade types, maintaining consistent performance over long production runs.

For applications requiring precise ink metering, extended durability, and reduced maintenance, the C2000 ceramic-coated doctor blade is an ideal choice. The dual-layer ceramic coating improves performance in spot color printing, full coverage designs, fine line printing, QR code printing, and leather applications. This blade performs well with corrosive inks, high-viscosity formulations, and metallic particle-based inks, ensuring long-lasting use while maintaining print quality.